Premixed based on hydraulic lime, special sulfur aluminate binders, water retainers, shrinkage compensators and reducers of the water/binder ratio, used for fixing and anchoring, in masonry, connectors, inserts, bars, brackets, grouting of the joints, tacking of lesions. It is a product with accelerated setting and hardening, with setting start at 30 ', end setting at 60' and development of mechanical strength already after 90 'of curing. Particularly recommended in the restoration of period and monumental buildings.
Conservabilité: 6 mois
Diamètre maximum agrégat: 0.5 mm
Mélanger avec de l'eau: 23 - 30 %
Poids spécifique: 1.97 kg/dm³
Pot-life: 15 min
Température d'utilisation: +5 / +30 °C
Utiliser en portant des gants de protection
< 0.50 kg•h^0.5/m²
Durcissement au toucher
> 1.0 N/mm²
Module élastique statique
> 12 _
Réaction au feu
Résistance à compression à 01 jour
> 13 MPa
Résistance à compression à 28 jours
> 20 MPa
Résistance à la compression après 1,5 heure
> 4 MPa
Résistance à la flexion à 01 jour
> 4 MPa
Résistance à la flexion à 28 jours
> 6 MPa
- Gris clair
- Sac 25 kg
- Palette: 50 x (Sac 25 kg)
The particularly fine constituent materials allow adequate anchoring even in the presence of a small space between hole and connectors. By mixing ANCHORSANA FIX with different water contents, the product passes from thixotropic consistencies (23% water) to fluid gel consistencies (30% water), allowing any type of anchoring, from overhead to inclinations towards the bass. The product does not contain resins and solvents and can also be used indoors, subject to the usual precautions necessary when handling materials based on alkaline and irritating powders such as lime (use suitable personal protective equipment, such as gloves and protective goggles).
Approximately 1.6 kg of ANCHORSANA FIX for each cubic decimeter of volume to be filled.
Fixing and anchoring, in masonry bodies, of rigid connectors, jib connectors, inserts, bars with improved adherence, anchors. It develops great adhesion on materials of different nature: metal, fiberglass, basalt.
Blow with compressed air and forced suction of the housing holes. The application surfaces must be clean, free of dirt, moving, crumbly and incoherent parts, dust, etc., suitably saturated with water until reaching the condition of "saturated with dry surface".
Pour about 2/3 of the mixing water into the mixer; gradually add ANCHORSANA FIX and the water still required, continuing to mix, until a homogeneous, lump-free mixture of the desired consistency is obtained. Apply with a trowel or by casting. The mixing water indicatively required is equal to 23% by weight for thixotropic doughs, and to 30% by weight for doughs with a plastic-fluid consistency.
- Mortiers de béton, à la chaux et mixtes
- Maçonneries mixtes
- Maçonneries en briques creuses
- Maçonneries en pierre
- Chapes de support